Glass formation in the ternary Zr-Zr2Cu-Zr2Ni system

H. Yang; J. Q. Wang; Y. Li

doi:10.1016/j.jnoncrysol.2006.01.083

Glass formation in the ternary Zr-Zr₂Cu-Zr₂Ni system

H. Yang
, J. Q. Wang^*
, Y. Li

^*Corresponding author for this work

CAS - Institute of Metal Research
National University of Singapore

Research output: Contribution to journal › Article › peer-review

15 Scopus citations

Abstract

Glass formation and glass forming ability in the ternary Zr-Cu-Ni system were studied systematically. For Cu mold casting, the critical size for glass formation was found to be 1 mm in a relatively wide composition range of 56-64 at.% Zr, 16-26 at.% Cu and 16-24 at.% Ni. The phases competing with glass formation were found to be Zr, Zr₂Cu and Zr₂Ni. Despite the fact that Cu and Ni are completely miscible with each other, they cannot be regarded as simple substitution to each other in the case of glass formation in the Zr-Zr₂Cu-Zr₂Ni ternary eutectic system.

Original language	English
Pages (from-to)	832-836
Number of pages	5
Journal	Journal of Non-Crystalline Solids
Volume	352
Issue number	8
DOIs	https://doi.org/10.1016/j.jnoncrysol.2006.01.083
State	Published - 1 Jun 2006
Externally published	Yes

Keywords

Amorphous metals
Calorimetry
Glass formation
Glass transition
Metallic glasses
Thermal properties
Transition metals
X-ray diffraction

Access to Document

10.1016/j.jnoncrysol.2006.01.083

Cite this

@article{08e8fef20ba74cf3b58d10363b9fa754,

title = "Glass formation in the ternary Zr-Zr2Cu-Zr2Ni system",

abstract = "Glass formation and glass forming ability in the ternary Zr-Cu-Ni system were studied systematically. For Cu mold casting, the critical size for glass formation was found to be 1 mm in a relatively wide composition range of 56-64 at.\% Zr, 16-26 at.\% Cu and 16-24 at.\% Ni. The phases competing with glass formation were found to be Zr, Zr2Cu and Zr2Ni. Despite the fact that Cu and Ni are completely miscible with each other, they cannot be regarded as simple substitution to each other in the case of glass formation in the Zr-Zr2Cu-Zr2Ni ternary eutectic system.",

keywords = "Amorphous metals, Calorimetry, Glass formation, Glass transition, Metallic glasses, Thermal properties, Transition metals, X-ray diffraction",

author = "H. Yang and Wang, \{J. Q.\} and Y. Li",

year = "2006",

month = jun,

day = "1",

doi = "10.1016/j.jnoncrysol.2006.01.083",

language = "英语",

volume = "352",

pages = "832--836",

journal = "Journal of Non-Crystalline Solids",

issn = "0022-3093",

publisher = "Elsevier B.V.",

number = "8",

}

TY - JOUR

T1 - Glass formation in the ternary Zr-Zr2Cu-Zr2Ni system

AU - Yang, H.

AU - Wang, J. Q.

AU - Li, Y.

PY - 2006/6/1

Y1 - 2006/6/1

N2 - Glass formation and glass forming ability in the ternary Zr-Cu-Ni system were studied systematically. For Cu mold casting, the critical size for glass formation was found to be 1 mm in a relatively wide composition range of 56-64 at.% Zr, 16-26 at.% Cu and 16-24 at.% Ni. The phases competing with glass formation were found to be Zr, Zr2Cu and Zr2Ni. Despite the fact that Cu and Ni are completely miscible with each other, they cannot be regarded as simple substitution to each other in the case of glass formation in the Zr-Zr2Cu-Zr2Ni ternary eutectic system.

AB - Glass formation and glass forming ability in the ternary Zr-Cu-Ni system were studied systematically. For Cu mold casting, the critical size for glass formation was found to be 1 mm in a relatively wide composition range of 56-64 at.% Zr, 16-26 at.% Cu and 16-24 at.% Ni. The phases competing with glass formation were found to be Zr, Zr2Cu and Zr2Ni. Despite the fact that Cu and Ni are completely miscible with each other, they cannot be regarded as simple substitution to each other in the case of glass formation in the Zr-Zr2Cu-Zr2Ni ternary eutectic system.

KW - Amorphous metals

KW - Calorimetry

KW - Glass formation

KW - Glass transition

KW - Metallic glasses

KW - Thermal properties

KW - Transition metals

KW - X-ray diffraction

UR - https://www.scopus.com/pages/publications/33646138267

U2 - 10.1016/j.jnoncrysol.2006.01.083

DO - 10.1016/j.jnoncrysol.2006.01.083

M3 - 文章

AN - SCOPUS:33646138267

SN - 0022-3093

VL - 352

SP - 832

EP - 836

JO - Journal of Non-Crystalline Solids

JF - Journal of Non-Crystalline Solids

IS - 8

ER -

Glass formation in the ternary Zr-Zr₂Cu-Zr₂Ni system

Abstract

Keywords

Access to Document

Other files and links

Fingerprint

Cite this