Alkaline aluminum phosphate glasses for thermal ion-exchanged optical waveguide

Alkaline aluminum phosphate glasses (NMAP) with excellent chemical durability for thermal ion-exchanged optical waveguide have been designed and investigated. The transition temperature Tg (470 °C) is higher than the ion-exchange temperature (390 °C), which is favorable to sustain the stability of the glass structure for planar waveguide fabrication. The effective diffusion coefficient D_e of K⁺-Na⁺ ion exchange in NMAP glasses is 0.110 μm²/min, indicating that ion exchange can be achieved efficiently in the optical glasses. Single-mode channel waveguide has been fabricated on Er³⁺/Yb³⁺ doped NMAP glass substrate by standard micro-fabrication and K⁺-Na⁺ ion exchange. The mode field diameter is 9.6 μm in the horizontal direction and 6.0 μm in the vertical direction, respectively, indicating an excellent overlap with a standard single-mode fiber. Judd-Ofelt intensity parameter Ω₂ is 5.47 × 10^-20 cm², implying a strong asymmetrical and covalent environment around Er³⁺ in the optical glasses. The full width at half maximum and maximum stimulated emission cross section of the ⁴I_13/2 → ⁴I_15/2 are 30 nm and 6.80 × 10^-21 cm², respectively, demonstrating that the phosphate glasses are potential glass candidates in developing compact optoelectronic devices. Pr³⁺, Tm³⁺ and Ho³⁺ doped NMAP glasses are promising candidates to fabricate waveguide amplifiers and lasers operating at special telecommunication windows.