Crystal growth and photorefractive properties of (Cu,Ce)-doped KNSBN crystal

Y. L. Zhang; E. Y.B. Pun; D. X. Lu; E. M.W. Wong; P. S. Chung; D. Mo

Crystal growth and photorefractive properties of (Cu,Ce)-doped KNSBN crystal

Y. L. Zhang^*
, E. Y.B. Pun
, D. X. Lu
, E. M.W. Wong
, P. S. Chung
, D. Mo

^*此作品的通讯作者

City University of Hong Kong

科研成果: 会议稿件 › 论文 › 同行评审

摘要

KNSBN crystal has been grown successfully with both Cu & Ce dopings. It is found that the Cu & Ce dopings increase effectively the absorption of KNSBN crystal and enhance the photorefractive properties at wavelengths 400-650 nm. Two-wave mixing and self-pumped phase conjugation experiments were carried out on these crystals at 632.8 nm. The two-wave coupling gain and the self-pumped phase conjugation reflectivity were measured to be as large as 10 cm^-1 and 70%, respectively.

源语言	英语
页	679-682
页数	4
出版状态	已出版 - 1996
已对外发布	是
活动	Proceedings of the 1996 10th IEEE International Symposium on Applications of Ferroelectrics, ISAF. Part 1 (of 2) - East Brunswick, NJ, USA 期限: 18 8月 1996 → 21 8月 1996

会议

会议	Proceedings of the 1996 10th IEEE International Symposium on Applications of Ferroelectrics, ISAF. Part 1 (of 2)
市	East Brunswick, NJ, USA
时期	18/08/96 → 21/08/96

其它文件与链接

链接到 Scopus 的出版物

引用此

@conference{0418d0e1b8554db3808e859f3b90080c,

title = "Crystal growth and photorefractive properties of (Cu,Ce)-doped KNSBN crystal",

abstract = "KNSBN crystal has been grown successfully with both Cu \& Ce dopings. It is found that the Cu \& Ce dopings increase effectively the absorption of KNSBN crystal and enhance the photorefractive properties at wavelengths 400-650 nm. Two-wave mixing and self-pumped phase conjugation experiments were carried out on these crystals at 632.8 nm. The two-wave coupling gain and the self-pumped phase conjugation reflectivity were measured to be as large as 10 cm-1 and 70\%, respectively.",

author = "Zhang, \{Y. L.\} and Pun, \{E. Y.B.\} and Lu, \{D. X.\} and Wong, \{E. M.W.\} and Chung, \{P. S.\} and D. Mo",

year = "1996",

language = "英语",

pages = "679--682",

note = "Proceedings of the 1996 10th IEEE International Symposium on Applications of Ferroelectrics, ISAF. Part 1 (of 2) ; Conference date: 18-08-1996 Through 21-08-1996",

}

TY - CONF

T1 - Crystal growth and photorefractive properties of (Cu,Ce)-doped KNSBN crystal

AU - Zhang, Y. L.

AU - Pun, E. Y.B.

AU - Lu, D. X.

AU - Wong, E. M.W.

AU - Chung, P. S.

AU - Mo, D.

PY - 1996

Y1 - 1996

N2 - KNSBN crystal has been grown successfully with both Cu & Ce dopings. It is found that the Cu & Ce dopings increase effectively the absorption of KNSBN crystal and enhance the photorefractive properties at wavelengths 400-650 nm. Two-wave mixing and self-pumped phase conjugation experiments were carried out on these crystals at 632.8 nm. The two-wave coupling gain and the self-pumped phase conjugation reflectivity were measured to be as large as 10 cm-1 and 70%, respectively.

AB - KNSBN crystal has been grown successfully with both Cu & Ce dopings. It is found that the Cu & Ce dopings increase effectively the absorption of KNSBN crystal and enhance the photorefractive properties at wavelengths 400-650 nm. Two-wave mixing and self-pumped phase conjugation experiments were carried out on these crystals at 632.8 nm. The two-wave coupling gain and the self-pumped phase conjugation reflectivity were measured to be as large as 10 cm-1 and 70%, respectively.

UR - https://www.scopus.com/pages/publications/0030374618

M3 - 论文

AN - SCOPUS:0030374618

SP - 679

EP - 682

T2 - Proceedings of the 1996 10th IEEE International Symposium on Applications of Ferroelectrics, ISAF. Part 1 (of 2)

Y2 - 18 August 1996 through 21 August 1996

ER -

Crystal growth and photorefractive properties of (Cu,Ce)-doped KNSBN crystal

摘要

会议

其它文件与链接

学术指纹

引用此