Diffusivity, solubility and thermodynamic modelling of diffusion growth of Ga3+-doped LiTaO3 thin film for integrated optics

  • De Long Zhang*
  • , Qun Zhang
  • , Pei Zhang
  • , Jian Kang
  • , Wing Han Wong
  • , Dao Yin Yu
  • , Edwin Yue Bun Pun
  • *此作品的通讯作者
  • Tianjin University
  • Tianjin Sino-German University of Applied Sciences
  • City University of Hong Kong

科研成果: 期刊稿件文章同行评审

摘要

A thermodynamic study was performed on diffusion growth of Ga3+-doped LiTaO3(LT) thin film for integrated optics. Some Ga3+-doped LT thin films were grown on LT surface by in-diffusion of homogeneously coated Ga2O3 film at the temperature range of (1273 to 1473) K. After growth, the refractive indices at Ga3+-doped and un-doped surface parts were measured by prism coupling technique and Li composition there was evaluated from the measured refractive indices. The results show that Ga3+ dopant has small effect on the LT index. Li2O out-diffusion is not measurable. The Ga3+ profile in the grown thin film was analysed by secondary ion mass spectrometry. It is found that the grown Ga3+ ions follow a complementary error function profile. A thermodynamic model for Ga3+ diffusion growth is suggested and verified experimentally. From the measured Ga3+ profiles, some thermodynamic parameters were obtained. These include diffusivity, diffusion constant, chemical activation energy, solubility, solubility constant and enthalpy of solution. These parameters are crucial to design and growth of a desired Ga3+-doped LT thin film for integrated optics. Comparison shows that Ga3+ grows in LT two orders faster than Ti4+ because of its smaller radius. Ga3+ diffusivity/solubility in LT is one order/1.5-fold lower than in LiNbO3 because Ta has a larger atomic mass and hence a lower mobility than Nb.

源语言英语
页(从-至)93-99
页数7
期刊Journal of Chemical Thermodynamics
97
DOI
出版状态已出版 - 1 6月 2016
已对外发布

学术指纹

探究 'Diffusivity, solubility and thermodynamic modelling of diffusion growth of Ga3+-doped LiTaO3 thin film for integrated optics' 的科研主题。它们共同构成独一无二的学术指纹。

引用此