Emission characteristics of Er³⁺ in vapor-transport-equilibrated Er/Zn-codoped LiNbO₃ crystals

Polarized visible and infrared emission characteristics of Er³⁺ ions in vapor-transport-equilibration (VTE)-treated LiNbO₃ crystals codoped with different concentrations of Zn and Er were investigated in comparison with corresponding as-grown crystals. The results show that the VTE treatment leads to substantial spectral changes of Er³⁺ emissions at 0.65, 0.98 and 1.5 μm regions, and the spectral changes in the 0.98 and 1.5 μm regions appear to be Zn-concentration-dependent. It is concluded in combination with X-ray powder diffraction results and optical absorption characteristics reported previously that the VTE treatment resulted in crystalline phase transformation with respect to Er³⁺ ions from original LiNbO₃ to ErNbO₄ phase in all crystals studied. The formation of the ErNbO₄ phase and the Zn²⁺ codopants are responsible for the VTE-induced substantial spectral changes. The emission characteristics of the ErNbO₄ precipitates in the Zn/Er-codoped crystals are found to be very different from those of the ErNbO₄ precipitates in the only Er-doped crystal in the infrared region, and the difference is attributed to the influence of the Zn²⁺ codopant on the Er³⁺ ion environment. The mechanism of the crystalline phase transformation is qualitatively explained from the viewpoint of the declined solubility of Er³⁺ ion in a Li-rich LiNbO₃ crystal and from the phase diagram of Li₂O-Nb₂O₅ system.