Optical properties of Eu3+ in transparent Y-Ti-O nanocrystallized sol-gel film

B. J. Chen; L. Lin; X. J. Li; E. Y.B. Pun; H. Lin

doi:10.1016/j.jallcom.2009.05.104

Optical properties of Eu³⁺ in transparent Y-Ti-O nanocrystallized sol-gel film

B. J. Chen
, L. Lin
, X. J. Li
, E. Y.B. Pun
, H. Lin^*

^*此作品的通讯作者

City University of Hong Kong
Dalian Polytechnic University
Dalian Medical University

科研成果: 期刊稿件 › 快报 › 同行评审

2 引用（Scopus）

摘要

Transparent Y-Ti-O nanocrystallized layer was formed in Eu³⁺ doped sol-gel film after annealing at 600 °C. The crystalline particles have been proved to be a single cubic phase of Y-Ti-O and the mean size is identified to be 15.3 nm. Red fluorescence was clearly observed under the excitation of UV radiation. Experimental intensity parameters Ω₂ and Ω₄ of the Eu³⁺ doped nanocrystallized film system are calculated to be 4.02 × 10^-20 and 2.17 × 10^-20 cm², respectively, indicating a lack of the inversion symmetry of Eu³⁺ sites and an average covalent environment surrounding Eu³⁺ ions. The controllable homogeneous Y-Ti-O nanocrystallizations in the sol-gel films provide possibilities in developing illumination, display, optical detection and light conversion devices.

源语言	英语
页（从-至）	L5-L8
期刊	Journal of Alloys and Compounds
卷	485
期	1-2
DOI	https://doi.org/10.1016/j.jallcom.2009.05.104
出版状态	已出版 - 19 10月 2009
已对外发布	是

访问文件

10.1016/j.jallcom.2009.05.104

其它文件与链接

链接到 Scopus 的出版物

引用此

@article{28a23189962947bfba30c21659245198,

title = "Optical properties of Eu3+ in transparent Y-Ti-O nanocrystallized sol-gel film",

abstract = "Transparent Y-Ti-O nanocrystallized layer was formed in Eu3+ doped sol-gel film after annealing at 600 °C. The crystalline particles have been proved to be a single cubic phase of Y-Ti-O and the mean size is identified to be 15.3 nm. Red fluorescence was clearly observed under the excitation of UV radiation. Experimental intensity parameters Ω2 and Ω4 of the Eu3+ doped nanocrystallized film system are calculated to be 4.02 {\texttimes} 10-20 and 2.17 {\texttimes} 10-20 cm2, respectively, indicating a lack of the inversion symmetry of Eu3+ sites and an average covalent environment surrounding Eu3+ ions. The controllable homogeneous Y-Ti-O nanocrystallizations in the sol-gel films provide possibilities in developing illumination, display, optical detection and light conversion devices.",

keywords = "Europium, Nanocrystallizations, Sol-gel film, Spectral parameters, Y-Ti-O crystalline phase",

author = "Chen, \{B. J.\} and L. Lin and Li, \{X. J.\} and Pun, \{E. Y.B.\} and H. Lin",

year = "2009",

month = oct,

day = "19",

doi = "10.1016/j.jallcom.2009.05.104",

language = "英语",

volume = "485",

pages = "L5--L8",

journal = "Journal of Alloys and Compounds",

issn = "0925-8388",

publisher = "Elsevier B.V.",

number = "1-2",

}

TY - JOUR

T1 - Optical properties of Eu3+ in transparent Y-Ti-O nanocrystallized sol-gel film

AU - Chen, B. J.

AU - Lin, L.

AU - Li, X. J.

AU - Pun, E. Y.B.

AU - Lin, H.

PY - 2009/10/19

Y1 - 2009/10/19

N2 - Transparent Y-Ti-O nanocrystallized layer was formed in Eu3+ doped sol-gel film after annealing at 600 °C. The crystalline particles have been proved to be a single cubic phase of Y-Ti-O and the mean size is identified to be 15.3 nm. Red fluorescence was clearly observed under the excitation of UV radiation. Experimental intensity parameters Ω2 and Ω4 of the Eu3+ doped nanocrystallized film system are calculated to be 4.02 × 10-20 and 2.17 × 10-20 cm2, respectively, indicating a lack of the inversion symmetry of Eu3+ sites and an average covalent environment surrounding Eu3+ ions. The controllable homogeneous Y-Ti-O nanocrystallizations in the sol-gel films provide possibilities in developing illumination, display, optical detection and light conversion devices.

AB - Transparent Y-Ti-O nanocrystallized layer was formed in Eu3+ doped sol-gel film after annealing at 600 °C. The crystalline particles have been proved to be a single cubic phase of Y-Ti-O and the mean size is identified to be 15.3 nm. Red fluorescence was clearly observed under the excitation of UV radiation. Experimental intensity parameters Ω2 and Ω4 of the Eu3+ doped nanocrystallized film system are calculated to be 4.02 × 10-20 and 2.17 × 10-20 cm2, respectively, indicating a lack of the inversion symmetry of Eu3+ sites and an average covalent environment surrounding Eu3+ ions. The controllable homogeneous Y-Ti-O nanocrystallizations in the sol-gel films provide possibilities in developing illumination, display, optical detection and light conversion devices.

KW - Europium

KW - Nanocrystallizations

KW - Sol-gel film

KW - Spectral parameters

KW - Y-Ti-O crystalline phase

UR - https://www.scopus.com/pages/publications/72049110222

U2 - 10.1016/j.jallcom.2009.05.104

DO - 10.1016/j.jallcom.2009.05.104

M3 - 快报

AN - SCOPUS:72049110222

SN - 0925-8388

VL - 485

SP - L5-L8

JO - Journal of Alloys and Compounds

JF - Journal of Alloys and Compounds

IS - 1-2

ER -

Optical properties of Eu3+ in transparent Y-Ti-O nanocrystallized sol-gel film

摘要

访问文件

其它文件与链接

学术指纹

引用此

Optical properties of Eu³⁺ in transparent Y-Ti-O nanocrystallized sol-gel film